APPLICABILITY OF BITUMINOUS-BASED INHIBITOR AS CORROSION PREVENTION METHOD IN REINFORCED CONCRETE

  • Pinta Astuti Universitas Muhammadiyah Yogyakarta, Department of Civil Engineering, Jalan Brawijaya, Tamantirto, Kasihan, Bantul, Daerah Istimewa Yogyakarta, Indonesia
Keywords: bituminous-based inhibitor, corrosion prevention, half-cell potential, PCC, PPC

Abstract


Corrosion is the most common cause of structural and material degradation in reinforced concrete (RC) constructions. A well-constructed structure protects the embedded steel bar from chloride ions both physically and chemically, which is particularly important for constructions exposed to seawater. Given the significant economic losses caused by corrosion, suitable measures to reduce corrosion in concrete are required. In this study, three-layer of bituminous-based inhibitor was applied to the surface of two steel bars embedded (steel coating) in mortar cement with 3 cm and 5 cm of concrete cover. Portland composite cement (PCC) and Portland pozzolan cement (PPC) was used as a binder material of mortar cement. The cubical mortar cement specimens were fabricated, and exposed to three conditions (e.g., wet condition, dry condition, and dry-wet cycle) until 60 days after 28 days of immersed water curing. The results demonstrated that corrosion prevention employing steel coating techniques by using bituminous-based inhibitor gives superior protection as seen by a higher positive corrosion potential value when compared to non-coating specimens, implying that the coating method may be used to prevent corrosion. This is because the coating process by using bituminous-based inhibitor may prevent ions from entering the reinforcing steel. In all exposure circumstances and with all preventive procedures, a concrete cover with a thickness of 5 cm has a lower corrosion risk, as shown by a higher corrosion potential value, than a concrete cover with a thickness of 3 cm. The larger the thickness of the concrete cover, the more the surrounding ecosystem is protected. The utilization of PPC as binder in concrete maintained the stable corrosion potential value when the coating method applied.        

References

Shehnazdeep, & Pradhan, B. (2022). A study on effectiveness of inorganic and organic corrosion inhibitors on rebar corrosion in concrete: A review. Materials Today: Proceedings. https://doi.org/10.1016/j.matpr.2022.04.296

Zhang, X., Zhang, Y., Liu, B., Liu, B., Wu, W., & Yang, C. (2021). Corrosion-induced spalling of concrete cover and its effects on shear strength of RC beams. Engineering Failure Analysis, 127, 105538. https://doi.org/10.1016/j.engfailanal.2021.105538

Dasar, A., Hamada, H., Sagawa, Y., & Yamamoto, D. (2017). Deterioration progress and performance reduction of 40-year-old reinforced concrete beams in natural corrosion environments. Construction and Building Materials, 149, 690–704. https://doi.org/10.1016/j.conbuildmat.2017.05.162

Meiyan, H., Minghui, J., Wenlei, Z., Yubin, Y., Teng, C., & Hao, W. (2021). Composite salt corrosion deterioration characteristics and damage calculation models of concrete incorporated with corrosion inhibiting admixtures. Journal of Building Engineering, 44, 103221. https://doi.org/10.1016/j.jobe.2021.103221

Rodrigues, R., Gaboreau, S., Gance, J., Ignatiadis, I., & Betelu, S. (2021). Reinforced concrete structures: A review of corrosion mechanisms and advances in electrical methods for corrosion monitoring. Construction and Building Materials, 269, 121240. https://doi.org/10.1016/j.conbuildmat.2020.121240

El Maaddawy, T., & Soudki, K. (2007). A model for prediction of time from corrosion initiation to corrosion cracking. Cement and Concrete Composites, 29(3), 168–175. https://doi.org/10.1016/j.cemconcomp.2006.11.004

Khan, M. U., Ahmad, S., & Al-Gahtani, H. J. (2017). Chloride-induced corrosion of steel in concrete: An overview on chloride diffusion and prediction of corrosion initiation time. International Journal of Corrosion, 2017, 1–9. https://doi.org/10.1155/2017/5819202

Astuti, P., Kamarulzaman, K., Rafdinal, R. S., Hamada, H., Sagawa, Y., & Yamamoto, D. (2020). Influence of rust removal process on the effectiveness of sacrificial anode cathodic protection in repair concrete. IOP Conference Series: Materials Science and Engineering, 849(1), 012088. https://doi.org/10.1088/1757-899X/849/1/012088

Astuti, P., Rafdinal, R. S., Hamada, H., Sagawa, Y., Yamamoto, D., & Kamarulzaman, K. (2019). Effectiveness of rusted and non-rusted reinforcing bar protected by sacrificial anode cathodic protection in repaired patch concrete. In IOP Conference Series: Earth and Environmental Science. https://doi.org/10.1088/1755-1315/366/1/012013

Lozinguez, E., Barthélémy, J. F., Bouteiller, V., & Desbois, T. (2018). Contribution of sacrificial anode in reinforced concrete patch repair: Results of numerical simulations. Construction and Building Materials, 178, 405–417. https://doi.org/10.1016/j.conbuildmat.2018.05.063

Goyal, A., Ganjian, E., Pouya, H. S., & Tyrer, M. (2021). Inhibitor efficiency of migratory corrosion inhibitors to reduce corrosion in reinforced concrete exposed to high chloride environment. Construction and Building Materials, 303, 124461. https://doi.org/10.1016/j.conbuildmat.2021.124461

Teymouri, F., Allahkaram, S. R., Shekarchi, M., Azamian, I., & Johari, M. (2021). A comprehensive study on the inhibition behaviour of four carboxylate-based corrosion inhibitors focusing on efficiency drop after the optimum concentration for carbon steel in the simulated concrete pore solution. Construction and Building Materials, 296, 123702. https://doi.org/10.1016/j.conbuildmat.2021.123702

Harilal, M., et al. (2021). The chloride-induced corrosion of a fly ash concrete with nanoparticles and corrosion inhibitor. Construction and Building Materials, 274, 122097. https://doi.org/10.1016/j.conbuildmat.2020.122097

Wang, H., et al. (2020). Study on the influence of compound rust inhibitor on corrosion of steel bars in chloride concrete by electrical parameters. Construction and Building Materials, 262, 120763. https://doi.org/10.1016/j.conbuildmat.2020.120763

Song, Z., et al. (2021). Using ultrasonic wave to trigger microcapsule inhibitor against chloride-induced corrosion of carbon steel in simulated concrete pore solution. Construction and Building Materials, 311, 125331. https://doi.org/10.1016/j.conbuildmat.2021.125331

Hu, J., et al. (2021). The effect of organic core–shell corrosion inhibitors on corrosion performance of the reinforcement in simulated concrete pore solution. Construction and Building Materials, 267, 121011. https://doi.org/10.1016/j.conbuildmat.2020.121011

Ngo, T. T., Tran, N. T., Kim, D. J., & Pham, T. C. (2021). Effects of corrosion level and inhibitor on pullout behavior of deformed steel fiber embedded in high-performance concrete. Construction and Building Materials, 280, 122449. https://doi.org/10.1016/j.conbuildmat.2021.122449

Mohamed, A., Visco, D. P., & Bastidas, D. M. (2022). Effect of cations on the activity coefficient of no2-/no3- corrosion inhibitors in simulated concrete pore solution: An electrochemical thermodynamics study. Corrosion Science, 110476. https://doi.org/10.1016/j.corsci.2022.110476

Lapiro, I., Mezhov, A., & Kovler, K. (2022). Performance of corrosion inhibitors in reinforced concrete elements under electrical voltage. Construction and Building Materials, 342, 127656. https://doi.org/10.1016/j.conbuildmat.2022.127656

Das, J. K., & Pradhan, B. (2022). Study on influence of nitrite and phosphate-based inhibiting admixtures on chloride interaction, rebar corrosion, and microstructure of concrete subjected to different chloride exposures. Journal of Building Engineering, 50, 104192. https://doi.org/10.1016/j.jobe.2022.104192

Zhang, Y., et al. (2022). Inhibitor loaded functional HNTs modified coatings towards corrosion protection in reinforced concrete environment. Progress in Organic Coatings, 170, 106971. https://doi.org/10.1016/j.porgcoat.2022.106971

Wang, X. Y., Lee, S., & Cho, H. (2021). Penetration properties and injecting conditions of corrosion inhibitor for concrete. Construction and Building Materials, 284, 122761. https://doi.org/10.1016/j.conbuildmat.2021.122761

Yang, P., Gao, X., Wang, S., Su, J. F., & Wang, L. Q. (2022). Novel waterproof bituminous coating using self-healing microcapsules containing ultraviolet light curing agent. Construction and Building Materials, 329, 127189. https://doi.org/10.1016/j.conbuildmat.2022.127189

Zamanizadeh, H. R., Shishesaz, M. R., Danaee, I., & Zaarei, D. (2015). Investigation of the corrosion protection behavior of natural montmorillonite clay/bitumen nanocomposite coatings. Progress in Organic Coatings, 78, 256–260. https://doi.org/10.1016/j.porgcoat.2014.08.011

Kunthawatwong, R., et al. (2022). Recycled non-biodegradable polyethylene terephthalate waste as fine aggregate in fly ash geopolymer and cement mortars. Construction and Building Materials, 328, 127084. https://doi.org/10.1016/j.conbuildmat.2022.127084

Yu, S., Sanjayan, J., & Du, H. (2022). Effects of cement mortar characteristics on aggregate-bed 3D concrete printing. Construction and Building Materials, 332, 127405. https://doi.org/10.1016/j.conbuildmat.2022.127405

Subharaj, C., Logesh, M., Abdul Munaf, A., Srinivas, J., & Gnanaraj, S. J. P. (2022). Sustainable approach on cement mortar incorporating silica fume, LLDPE and sisal fiber. Materials Today: Proceedings. https://doi.org/10.1016/j.matpr.2022.06.361

Klyuev, S., et al. (2022). Fresh and mechanical properties of low-cement mortars for 3D printing. Construction and Building Materials, 338, 127644. https://doi.org/10.1016/j.conbuildmat.2022.127644

Nasir, M., et al. (2022). Engineered cellulose nanocrystals-based cement mortar from office paper waste: Flow, strength, microstructure, and thermal properties. Journal of Building Engineering, 51, 104345. https://doi.org/10.1016/j.jobe.2022.104345

Astuti, P., et al. (2024). Engineering properties of seawater-mixed mortar with batching plant residual waste as aggregate replacement. SINERGI, 28(2), 381. https://doi.org/10.22441/sinergi.2024.2.017

ASTM C4137. (2007). Standard test method for flow of hydraulic cement mortar. ASTM International.

SNI 1973:2016. (2016). Metode Uji Densitas, Volume Produksi Campuran dan Kadar Udara (Gravimetrik) Beton. Badan Standardisasi Nasional.

Elsener, B. (2001). Half-cell potential mapping to assess repair work on RC structures. Construction and Building Materials, 15(2–3), 133–139. https://doi.org/10.1016/s0950-0618(00)00062-3

Published
2024/06/24
Section
Original Scientific Paper