The influence of new severe plastic deformation on microstructure, mechanical, and corrosion properties of Mg-0.8Mn-0.5Ca alloy

  • Masood Khani 1- Department of Materials and Polymer Engineering, Hakim Sabzevari University, Sabzevar, Iran.
  • Gholamreza Ebrahimi Materials and Metallurgical Engineering Department, Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran. https://orcid.org/0000-0003-2549-3246
  • H.R. Ezatpour 4) Department of Materials Science and Engineering, Hamedan University of Technology, Hamedan, Iran.
  • Amir Momeni Department of Materials Science and Engineering, Hamedan University of Technology, Hamedan, Iran.
Keywords: Severe plastic deformation, Dynamic recrystallization, Hydroxyapatite, Hydrogen evolution, EIS test, Biocompatible

Abstract


In this research, the effect of accumulative extrusion bonding (AEB) on the microstructure and mechanical properties of Mg-0.8Mn-0.5Ca biocompatible alloy was investigated. The goal of this research was to develop the mechanical and corrosion properties of Mg-0.8Mn-0.5Ca alloy after ABE process as a novel severe plastic deformation process. The simulation of AEB process showed that the average effective strain per pass for channels with the internal angle of 120 was about 1.93. The average grain size was dramatically decreased from about 448.3 µm for the homogenized alloy to 1.55 µm for the 3-pass processed sample. Microstructural observations suggested a combination of continuous, discontinuous, and twinning-induced dynamic recrystallization as the major mechanisms of grain refinement. Tensile and compressive strengths were improved from 150 and 205 MPa to 330 and 301 MPa after three passes of AEB, indicating 2 and 1.5 times improvements, respectively. Tensile elongation decreased from 26% for the homogenized sample to 7.5% for the 3-pass processed sample due to the severe work-hardening, non-uniform strains, and inhomogeneous microstructure produced by the ABE process. Corrosion resistance in SBF solution was improved from 1.1 to 14.159 〖KΩ Cm〗^2 after three passes of ABE due to the presence of hydroxyapatite formed on the surface of the AEBed samples.

 

Author Biography

Masood Khani, 1- Department of Materials and Polymer Engineering, Hakim Sabzevari University, Sabzevar, Iran.

Masood Khani is my PhD student

References

[1] N. Li, Y. Zheng, J. Mater. Sci. Technol., 29 (6) (2013) 489-502.
[2] S. Hiromoto, T. Shishido, A. Yamamoto, N. Maruyama, H. Somekawa, T. Mukai. Corr. Sci., 50 (10) (2008) 2906-2913.
[3] S.K. Asl, S. Nemeth, M.J. Tan. Surf. Coat. Tech., 258 (2014) 931-937.
[4] X.N. Gu, N. Li, W.R. Zhou, Y.F. Zheng, X. Zhao, Q.Z. Cai, L. Ruan. Acta Biomater., 7 (4) (2011) 1880-1889.
[5] H.X. Wang, S.K. Guan, X. Wang, C.X. Ren, L.G. Wang. Acta. Biomater., 6 (5) (2010) 1743-1748.
[6] S. Agarwal, J. Curtin, B. Duffy, S. Jaiswal. Mater. Sci. Eng. C., 68 (2016) 948-963.
[7] J. Fan, X. Qiu, X. Niu, Z. Tian, W. Sun, X. Liu, Y. Li, W. Li. J. Meng, Mater. Sci. Eng. C., 33 (4) (2013) 2345-2352.
[8] T. Lei, W. Tang, S.H. Cai, F.F. Feng, N.F. Li. Corr. Sci., 54 (2012) 270-277.
[9] M.C. Turhan, Q. Li, H. Jha, R.F. Singer, S. Virtanen. Electrochim. Acta., 56 (20) (2011) 7141-7148.
[10] E.C. Meng, S.K. Guan, H.X. Wang, L.G. Wang. S.J. Zhu, J.H. Hu, C.X. Ren, J.H. Gao, Y.S. Feng. Appl. Surf. Sci., 257(11) (2011) 4811-4816.
[11] D.Orlov, G. Raab, T.T. Lamark, M. Popov, Y. Estrin. Acta. Mater., 59 (15) (2011) 375-385.
[12] X.N. Gu, Y.F. Zheng, Y. Cheng, S.P. Zhong, T.F. Xi. Biomater., 30 (4) (2009) 484-498.
[13] R. Radha, D. Sreekanth. J. Mag. Alloy., 5(3) (2017) 286-312.
[14] J.Z. Ilich, J.E. Kerstetter. J. Am. Coll. Nutr., 19(6) (2000) 715-737.
[15] C.M. Serre, M. Papillard, P. Chavassieux, J.C. Voegel, G. Boivin. J. Biomed. Mater. Res., 42 (4) (1998) 626-633.
[16] H.Y. Ha, H.J. Kim, S.M. Baek, S.D. Sohn, H.J. Shin, H.Y. Jeong, S.H. Park, C.D. Yim, B.S. You, J.G. Lee, S.S. Park. Scr. Mater., 109 (2015) 38-43.
[17] Y. Ding, C. Wen, P. Hodgson, Y. Li. J. Mater. Chem. B., 2(14) (2014) 1912-1933.
[18] Y. Ali, D. Qiu, B. Jiang, F. Pan, M.X. Zhang. J. Alloys Compd., 619 (2015) 639-651.
[19] F. Zhang, A. Ma, D. Song, J. Jiang, F. Lu, L. Zhang, D. Yang, J. Chen. J. Rare Earths., 33 (1) (2015) 93-101.
[20] S.Z. Khalajabadi, N. Ahmad, A. Yahya, M.A. Yajid., A. Samavati, S. Asadi, A. Arafat, M.R. Kadir. Ceram. Int., 42(16) (2016) 18223-18237.
[21] X. Wang, P. Zhang, L.H. Dong, X.L. Ma, J.T. Li, Y.F. Zheng. Mater. Des., 54 (2014) 995-1001.
[22] M. Razavi, M.H. Fathi, M. Meratian. Mater. Lett., 64 (22) (2010) 2487-2490.
[23] H. Wang, S. Guan, Y. Wang, H. Liu, H. Wang, L. Wang, C. Ren, S. Zhu, K. Chen. Colloids. Surf. B: Biointerfaces., 88 (1) (2011) 254-259.
[24] M. Li, Y. Cheng, Y.F. Zheng, X. Zhang, T.F. Xi, S.C. Wei. Surf. Coat. Tech., 228 (2013) 262-265.
[25] E.C. Meng, S.K. Guan, H.X. Wang, L.G. Wang, S.J. Zhu, J.H. Hu, C.X. Ren, J.H. Gao, Y.S. Feng. Surf. Sci., 257 (11) (2011) 4811-4816.
[26] R. Del Campo, B. Savoini, A. Munoz, M. A. Monge, R. Pareja. J. Mech. Behav. Biomed. Mater., 69 (2017) 135-143.
[27] Y. Huang, D. Liu, L. Anguilano, C. You, M. Chen. Mater. Sci. Eng. C., 54 (2015) 120-132.
[28] K.B. Nie, K.K. Deng, X.J. Wang, T.Wang, K. Wu. Mater. Charact., 124 (2017) 14.
[29] W. J. Kim, C. W. An, Y. S. Kim, S. I. Hong. Scr. Mater., 47 (1) (2002) 39.
[30] H.K. Kim. Mater. Sci. Eng. A., 515 (1-2) (2009) 66-70.
[31] S. M. Masoudpanah, R. Mahmudi. Mater. Des., 31 (7) (2010) 3512-3517.
[32] S.H. Lee, Y. Saito, N. Tsuji, H. Utsunomiya, T. Sakai. Scr. Mater., 46 (2002) 281.
[33] M. Alizadeh. Matr. Sci. Eng. A., 528 (2010) 578-582.
[34] S. Amirkhanlou, M. Ketabchi, N. Parvin, S. Khorsand, R. Bahrami. Mater. Des., 51 (2013) 367.
[35] G. I. Raab, E. P. Soshnikova, R. Z. Valiev. Mater. Sci. Eng. A., 387 (2004) 674-677.
[36] M. Eizadjou, H. D. Manesh, K. Janghorban. Mater Des., 30 (10) (2009) 4156-4146.
[37] R. Kocich, M. Greger, M. Kursa, I. Szurman, A. Macháčková. Mat. Sci. Eng. A., 527 (2010) 6386-6392.
[38] L. Olejnik, A. Rosochowski. Tech. Sci., 53 (2005) (4) 53.
[39] P. Bernard, S. Bag, K. Huang, R.E. Logé. Mater. Sci. Eng. A., 528 (2011) (24) 7357-7367.
[40] D.G. Cram, H.S. Zurob, Y.J.M. Brechet, C.R.A. Hutchinson. Acta. Mater., 57 (17) (2009) 5218-5228.
[41] F. Montheillet, O. Lurdos, G. Damamme. Acta. Mater., 57 (5) (2009) 1602-1612.
[42] F.J. Humphreys, M. hatherly, Recrystallization and Related Annealing Phenomena, second ed., Oxford, Pergamon, New York, 2004, p. 252.
. C. Author, The name of the Book, Publisher, City, 1997, p.123.
[43] A. Yamashita, Z. Horita, T.G. Langdon. Mater. Sci. Eng. A., 300 (2001) 142-147.
[44] R.B. Figueiredo, T.G. Langdon. Journal of materials science. Mater. Sci. Eng. A., 501 (2009) 105-114.
[45] K. Máthis, J. Gubicza, N.H. Nam. J. Alloys. Compd., 394 (2005) 194-199.
[46] R. Kaibyshev, O. Sitdikov. [c]// Mcnelley T D. Recrystallization and Related Phenomena. (ReX’96), Monterey: MIAS, 287 (1997).
[47] R.B. Figueiredo, T.G. Langdon. J. Mater. Sci ., 45 (17) (2010) 4827-4836.
[48] O. Sitdikov, R. Kaibyshev: Dynamic recrystallization in pure magnesium. Mater. Trans. 42 (9) (2001) 1928-1937.
[49] P. C. Wu, C. P. Chang, P. W. Kao. Mater. Sci. Eng. A., 374 (1-2) (2004) 196-203.
[50] P. Klimanek, A. Pötzsch. Mater. Sci. Eng. A., 324 (1-2) (2002) 145-150.
[51] C. W. Su, L. Lu, M. O. Lai. Mater. Sci. Eng. A. 434 (1-2) (2006) 227-236.
[52] L. Jin, D. Lin, D. Mao, X. Zeng, B. Chen, W. Ding. Mater. Sci. Eng. A., 423 (1-2) (2006) 247-252.
[53] A. S. Argon, J. Im, R. Safoglu. Metallurgical transactions A., 6 (4) (1975) 825.
[54] H. Miura, T. Maruoka, X. Yang, and J. J. Jonas. Scr. Mater., 66 (1) (2012) 49-51.
[55] R. Lapovok, P.F. Thomson, R. Cottam, Y. Estrin. J. Mater. Sci., 40 (7) (2005) 1699-1708.
[56] R. Radha, D. Sreekanth. J. Magnes. Alloy., 8(2) (2020) 452-60.
[57] M. H. Fathi, A. Hanifi, V. Mortazavi. J. Mater. Process. Technol., 202 (1-3) (2008) 536-542.
[58] D. Orlov, K.D. Ralston, N. Birbilis, Y. Estrin. Acta. Mater., 59 (15) (2011) 6176-6186.
[59] M. Eskandari, A. Zarei-Hanzaki, F. Pilehva, H.R. Abedi, S.M. Fatemi-Varzaneh, A.R. Khalesian. Mater. Sci. Eng. A., 576 (2013) 74-81.
Published
2023/12/28
How to Cite
Khani, M., Ebrahimi, G., Ezatpour, H., & Momeni, A. (2023). The influence of new severe plastic deformation on microstructure, mechanical, and corrosion properties of Mg-0.8Mn-0.5Ca alloy. Journal of Mining and Metallurgy, Section B: Metallurgy, 59(3), 515-530. Retrieved from https://aseestant.ceon.rs/index.php/jmm/article/view/28609
Issue
Vol. 59 No. 3 (2023)
Section
Original Scientific Paper

Authors retain copyright of the published papers and grant to the publisher the non-exclusive right to publish the article, to be cited as its original publisher in case of reuse, and to distribute it in all forms and media.

The Author(s) warrant that their manuscript is their original work that has not been published before; that it is not under consideration for publication elsewhere; and that its publication has been approved by all co-authors, if any, as well as tacitly or explicitly by the responsible authorities at the institution where the work was carried out. The Author(s) affirm that the article contains no unfounded or unlawful statements and does not violate the rights of others. The author(s) also affirm that they hold no conflict of interest that may affect the integrity of the Manuscript and the validity of the findings presented in it. The Corresponding author, as the signing author, warrants that he/she has full power to make this grant on behalf of the Author(s). Any software contained in the Supplemental Materials is free from viruses, contaminants or worms.

The published articles will be distributed under the Creative Commons Attribution ShareAlike 4.0 International license (CC BY-SA).

Authors are permitted to deposit publisher's version (PDF) of their work in an institutional repository, subject-based repository, author's personal website (including social networking sites, such as ResearchGate, Academia.edu, etc.), and/or departmental website at any time after publication.

Upon receiving the proofs, the Author(s) agree to promptly check the proofs carefully, correct any typographical errors, and authorize the publication of the corrected proofs.

The Corresponding author agrees to inform his/her co-authors, of any of the above terms.