Characterization of pre-alloyed NiTi powders produced by electrode induction-melting inert gas atomization for additive manufacturing
Abstract
In this research, the characteristics of Nickel-titanium (NiTi) powders produced by electrode induction melting inert gas atomization (EIGA) technique for additive manufacturing (AM) technology are investigated using various powder characterization technologies. The results show that the particle size distribution (PSD) of pre-alloyed NiTi powders prepared by EIGA has the range of 10 µm to 180 µm. The mean particle size distribution (D50) of the powder is 75 μm. The oxygen increase of the powder is only 0.005% compared to the raw rod. According to the requirements of the characteristics of the metal powder material used for AM, the powders are sieved into three categories, P1 (15-63 μm), P2 (63-150 μm), and P3 (>150 μm), respectively. The flow rates of P1 and P2 are 19.3 and 17.5 s∙(50 g)-1, respectively. The surface, cross- sectional microstructure, phase structure, and martensitic transformation temperature of the pre-alloyed NiTi powders with different particle sizes are investigated. The results show that powders of different particle sizes are primarily spherical or nearly spherical. The grain size of powders reduces with the decreasing of particle size. Both the bar stock and the powders of P1, P2, and P3 mainly exhibit the B2 phase. Comparing the powders P1, P2, and P3, the transformation temperature reduces with the decrease of particle size. A high density (99.55%) pre-alloyed NiTi specimen is successfully produced by selective laser melting (SLM) technology using P1 powders. The results indicate that the pre-alloyed NiTi alloy powder is appropriate for AM, which also has a good reference value for researchers producing AM powders.
Key Words: NiTi; Powder characteristics; EIGA; Selective laser melting; Martensitic transformation temperature
Authors retain copyright of the published papers and grant to the publisher the non-exclusive right to publish the article, to be cited as its original publisher in case of reuse, and to distribute it in all forms and media.
The Author(s) warrant that their manuscript is their original work that has not been published before; that it is not under consideration for publication elsewhere; and that its publication has been approved by all co-authors, if any, as well as tacitly or explicitly by the responsible authorities at the institution where the work was carried out. The Author(s) affirm that the article contains no unfounded or unlawful statements and does not violate the rights of others. The author(s) also affirm that they hold no conflict of interest that may affect the integrity of the Manuscript and the validity of the findings presented in it. The Corresponding author, as the signing author, warrants that he/she has full power to make this grant on behalf of the Author(s). Any software contained in the Supplemental Materials is free from viruses, contaminants or worms.The published articles will be distributed under the Creative Commons Attribution ShareAlike 4.0 International license (CC BY-SA).
Authors are permitted to deposit publisher's version (PDF) of their work in an institutional repository, subject-based repository, author's personal website (including social networking sites, such as ResearchGate, Academia.edu, etc.), and/or departmental website at any time after publication.
Upon receiving the proofs, the Author(s) agree to promptly check the proofs carefully, correct any typographical errors, and authorize the publication of the corrected proofs.
The Corresponding author agrees to inform his/her co-authors, of any of the above terms.