Study on the behavior of impurity removal from lithium iron phosphate slag using the ultrasonic-assisted sulphuric acid leaching
Abstract
Recovery of iron phosphate from the leaching slag of used lithium iron phosphate cathode materials is an important link to achieving closed-loop recovery of lithium iron phosphate, which has not yet been effectively achieved. The study used ultrasonic-assisted sulfuric acid leaching to remove impurity elements in iron phosphate to meet the requirements of battery-grade iron phosphate on the content of impurity elements. By optimizing the leaching conditions of sulfuric acid concentration of 0.2 mol∙L-1, ultrasonic acid leaching time of 30 min, ultrasonic power of 50 W, and reaction temperature of 80 ℃, the removal efficiencies of Cr, Cu, Ni, and Zn, the impurity elements in iron phosphate, were 26.09%, 83.0%, 75.9%, and 96.3%, respectively. At this time, the content of impurity elements Cr and Zn is in accordance with the standard for battery-grade iron phosphate (HG/T 4701-2021), with the content of 50ppm and 10ppm. The leaching results show that ultrasound is beneficial to the removal of impurity elements in iron phosphate in sulfuric acid solution. The results of XRD, particle size, TEM, and XPS analyses showed that the surface of the iron phosphate particles cavitated after ultrasonic acid leaching to form a large number of pores and the particles collided with the particle size became smaller, but there were no other by-products produced during the process. This process provides ideas to achieve the reuse of leaching slag (iron phosphate) and guides the recovery of metals from waste lithium iron phosphate cathode materials.
References
[1] J.-H. Li, X.-L. Zeng, A. Stevels, Ecodesign in consumer electronics: Past, Present, and Future, Critical Reviews in Environmental Science and Technology. 45 (2015) 840–860. https://doi.org/10.1080/10643389.2014.900245.
[2] J. Sencanski, D. Bajuk-bogdanovic, D. Majstorovic, E. Tchernychova, J. Papan, M. Vujkovic, The synthesis of Li(Co-Mn-Ni)O2 cathode material from spent-Li ion batteries and the proof of its functionality in aqueous lithium and sodium electrolytic solutions, Journal of Power Sources. 342 (2017) 690–703. https://doi.org/10.1016/j.jpowsour.2016.12.115.
[3] C.-W. Liu, J. Lin, H.-B. Cao, Y. Zhang, Z. Sun, Recycling of spent lithium-ion batteries in view of lithium recovery: A critical review, Journal of Cleaner Production. 228 (2019) 801–813. https://doi.org/10.1016/j.jclepro.2019.04.304.
[4] P. Byeon, H. Bin Bae, H.S. Chung, S.G. Lee, J.G. Kim, H.J. Lee, J.W. Choi, S.Y. Chung, Atomic-scale observation of LiFePO4 and LiCoO2 dissolution behavior in aqueous solutions, Advanced Functional Materials. 28 (2018) 1804564. https://doi.org/10.1002/adfm.201804564.
[5] J. Kumar, R.R. Neiber, J. Park, R.A. Soomro, G.W. Greene, S.A. Mazari, H.Y. Seo, J.H. Lee, M. Shon, D.W. Chang, K.Y. Cho, Recent progress in sustainable recycling of LiFePO4-type lithium-ion batteries: Strategies for highly selective lithium recovery, Chemical Engineering Journal. 431 (2022) 133993. https://doi.org/10.1016/j.cej.2021.133993.
[6] S. Gu, L. Zhang, B.-T. Fu, X.-P. Wang, J.W. Ahn, Feasible route for the recovery of strategic metals from mixed lithium-ion batteries cathode materials by precipitation and carbonation, Chemical Engineering Journal. 420 (2020) 127561. https://doi.org/10.1016/j.cej.2020.127561.
[7] W.-B. Lou, Y. Zhang, Y. Zhang, S.-L. Zheng, P. Sun, X.-J. Wang, S. Qiao, J.-Z. Li, Y. Zhang, D.-Y. Liu, M. Wenzel, J.-J. Weigand, A facile way to regenerate FePO4∙2H2O precursor from spent lithium iron phosphate cathode powder:spontaneous precipitation and phase transformation in an acidic medium, Journal of Alloys and Compounds. 856 (2020) 158148. https://doi.org/10.1016/j.jallcom.2020.158148.
[8] H. Mahandra, A. Ghahreman, A sustainable process for selective recovery of lithium as lithium phosphate from spent LiFePO4 batteries, Resources Conservation and Recycling. 175 (2021) 105883. https://doi.org/10.1016/j.resconrec.2021.105883.
[9] P. Moazzam, Y. Boroumand, P. Rabiei, S.S. Baghbaderani, P. Mokarian, F. Mohagheghian, L.J. Mohammed, A. Razmjou, Lithium bioleaching: An emerging approach for the recovery of Li from spent lithium ion batteries, Chemosphere. 277 (2021) 130196. https://doi.org/10.1016/j.chemosphere.2021.130196.
[10] X.-H. Zheng, Z.-W. Zhu, X. Lin, Y. Zhang, Y. He, H.-B. Cao, Z. Sun, A mini-review on metal recycling from spent lithium ion batteries, Engineering. 4 (2018) 361–370. https://doi.org/10.1016/j.eng.2018.05.018.
[11] X.-P. Chen, B.-L. Fan, L.-P. Xu, T. Zhou, J.-R. Kong, An atom-economic process for the recovery of high value-added metals from spent lithium-ion batteries, Journal of Cleaner Production. 112 (2015) 3562–3570. https://doi.org/10.1016/j.jclepro.2015.10.132.
[12] Y.-X. Yang, X.-H. Zheng, H.-B. Cao, C.-L. Zhao, X. Lin, P.-G. Ning, Y. Zhang, W. Jin, Z. Sun, A closed-loop process for selective metal recovery from spent lithium iron phosphate batteries through mechanochemical activation, ACS Sustainable Chemistry & Engineering. 5 (2017) 9972–9980. https://doi.org/10.1021/acssuschemeng.7b01914.
[13] W.-F. Gao, X.-H. Zhang, X.-H. Zheng, X. Lin, H.-B. Cao, Y. Zhi, Z. Sun, Lithium carbonate recovery from cathode scrap of spent lithium-ion battery– A closed-loop process, Environmental Science & Technology. 51 (2017) 1662–1669. https://doi.org/10.1021/acs.est.6b03320.
[14] D.-Y. Wu, D.-X. Wang, Z.-Q. Liu, S. Rao, K.-F. Zhang, Selective recovery of lithium from spent lithium iron phosphate batteries using oxidation pressure sulfuric acid leaching system, Transactions of Nonferrous Metals Society of China. 32 (2022) 2071–2079. https://doi.org/10.1016/S1003-6326(22)65931-4.
[15] S. Ghassa, A. Farzanegan, M. Gharabaghi, H. Abdollahi, Iron scrap, a sustainable reducing agent for waste lithium ions batteries leaching: An environmentally friendly method to treating waste with waste, Resources Conservation and Recycling. 166 (2021) 105348. https://doi.org/10.1016/j.resconrec.2020.105348.
[16] P.-C. Ning, Q. Meng, P. Dong, J.-G. Duan, M.-L. Xu, Y. Lin, Y.-J. Zhang, Recycling of cathode material from spent lithium ion batteries using an ultrasound-assisted DL-malic acid leaching system, Waste Management. 103 (2020) 52–60. https://doi.org/10.1016/j.wasman.2019.12.002.
[17] L.-Q. Zhuang, C.-H. Sun, T. Zhou, H. Li, A.-Q. Dai, Recovery of valuable metals from LiNi0.5Co0.2Mn0.3O2 cathode materials of spent Li-ion batteries using mild mixed acid as leachant, Waste Management. 85 (2019) 175–185. https://doi.org/10.1016/j.wasman.2018.12.034.
[18] L. Li, W.-J. Qu, X.-X. Zhang, J. Lu, R.-J. Chen, F. Wu, K. Amine, Succinic acid-based leaching system: A sustainable process for recovery of valuable metals from spent Li-ion batteries, Journal of Power Sources. 282 (2015) 544–551. https://doi.org/10.1016/j.jpowsour.2015.02.073.
[19] M. Esmaeili, S.O. Rastegar, R. Beigzadeh, T. Gu, Ultrasound-assisted leaching of spent lithium ion batteries by natural organic acids and H2O2, Chemosphere. 254 (2020) 126670. https://doi.org/10.1016/j.chemosphere.2020.126670.
[20] L.-M. Yang, Y.-F. Feng, C.-Q. Wang, D.-F. Fang, G.-P. Yi, Z. Gao, P.-H. Shao, C.-L. Liu, X.-B. Luo, S.-L. Luo, Closed-loop regeneration of battery-grade FePO4 from lithium extraction slag of spent Li-ion batteries via phosphoric acid mixture selective leaching, Chemical Engineering Journal. 431 (2022) 133232. https://doi.org/10.1016/j.cej.2021.133232.
[21] M. Dular, O.C. Delgosha, M. Petkovšek, Observations of cavitation erosion pit formation, Ultrasonics Sonochemistry. 20 (2013) 1113–1120. https://doi.org/10.1016/j.ultsonch.2013.01.011.
[22] F. Jiang, Y.-Q. Chen, S.-H. Ju, Q.-Y. Zhu, L.-B. Zhang, J.-H. Peng, X.-M. Wang, J.D. Miller, Ultrasound-assisted leaching of cobalt and lithium from spent lithium-ion batteries, Ultrasonics Sonochemistry. 48 (2018) 88–95. https://doi.org/10.1016/j.ultsonch.2018.05.019.
[23] L. Castro, R. Dedryvère, M. El Khalifi, P.E. Lippens, J. Bréger, C. Tessier, D. Gonbeau, The spin-polarized electronic structure of LiFePO4 and FePO4 evidenced by in-lab XPS, Journal of Physical Chemistry C. 114 (2010) 17995–18000. https://doi.org/10.1021/jp106631v.
[24] Z. Li, D.-F Liu, J.-C. Xiong, L.-H. He, Z.-W. Zhao, D.-Z. Wang, Selective recovery of lithium and iron phosphate/carbon from spent lithium iron phosphate cathode material by anionic membrane slurry electrolysis, Waste Management. 107 (2020) 1–8. https://doi.org/10.1016/j.wasman.2020.03.017.
[25] X.-J. Wang, S.-L. Zheng, Y. Zhang, Y. Zhang, S. Qiao, Z.-Q. Long, B. Zhao, Z.-F. Li, Sulfuric acid leaching of ball-milling activated FePO4 residue after lithium extraction from spent lithium iron phosphate cathode powder, Waste Management. 153 (2022) 31–40. https://doi.org/10.1016/j.wasman.2022.08.009.
Authors retain copyright of the published papers and grant to the publisher the non-exclusive right to publish the article, to be cited as its original publisher in case of reuse, and to distribute it in all forms and media.
The Author(s) warrant that their manuscript is their original work that has not been published before; that it is not under consideration for publication elsewhere; and that its publication has been approved by all co-authors, if any, as well as tacitly or explicitly by the responsible authorities at the institution where the work was carried out. The Author(s) affirm that the article contains no unfounded or unlawful statements and does not violate the rights of others. The author(s) also affirm that they hold no conflict of interest that may affect the integrity of the Manuscript and the validity of the findings presented in it. The Corresponding author, as the signing author, warrants that he/she has full power to make this grant on behalf of the Author(s). Any software contained in the Supplemental Materials is free from viruses, contaminants or worms.The published articles will be distributed under the Creative Commons Attribution ShareAlike 4.0 International license (CC BY-SA).
Authors are permitted to deposit publisher's version (PDF) of their work in an institutional repository, subject-based repository, author's personal website (including social networking sites, such as ResearchGate, Academia.edu, etc.), and/or departmental website at any time after publication.
Upon receiving the proofs, the Author(s) agree to promptly check the proofs carefully, correct any typographical errors, and authorize the publication of the corrected proofs.
The Corresponding author agrees to inform his/her co-authors, of any of the above terms.