Optimizing calcium additions for a strength–corrosion resistance balance in squeeze-cast Zn–Al–Cu–Mg alloys

  • THIYAGESAN G Research Scholar, National Institute of Technology, Tiruchirappalli
  • SankaraRaman Sankaranarayanan Professor, National Institute of Technology, Tiruchirappalli
  • S.P. Kumaresh Babu Professor, National Institute of Technology, Tiruchirappalli
Keywords: Squeeze casting; Zinc-Aluminium Alloy; Mechanical properties; Corrosion resistance.

Abstract


In this study, squeeze-cast Zn–Al–Cu–Mg alloys with varying Ca additions (0, 0.5, 1.0, and 1.5 wt.%) were investigated to evaluate the combined effects of microstructural evolution on mechanical and corrosion performance. Microstructural analysis showed a transition from coarse Zn-rich dendrites in the base alloy to a refined and uniform morphology with Ca additions up to 1.0 wt.%, followed by coarsening and increased porosity at 1.5 wt.% Ca due to excessive intermetallic formation. Mechanical testing indicated that the alloy with 1.0 wt.% Ca had the highest hardness (141 HV0.1) and tensile strength (359 MPa), attributed to grain refinement and dispersion strengthening, though with reduced ductility due to intermetallic brittleness. Electrochemical corrosion tests in 3.5 wt.% NaCl solution showed that the corrosion rate decreased from the base alloy to 1.0 wt.% Ca, confirming enhanced corrosion resistance due to microstructural refinement and protective film formation. However, excessive Ca addition (1.5 wt.%) increased the corrosion rate to 0.8109 mpy due to coarse intermetallics and porosity, which promoted localized attack. The results highlight that optimal Ca addition (1.0 wt.%) achieves a balance between strength, hardness, and corrosion resistance, making Ca-modified Zn–Al–Cu–Mg alloys promising candidates for structural and functional applications.

Published
2025/12/19
How to Cite
G, T., Sankaranarayanan, S., & Kumaresh Babu, S. (2025). Optimizing calcium additions for a strength–corrosion resistance balance in squeeze-cast Zn–Al–Cu–Mg alloys. Journal of Mining and Metallurgy, Section B: Metallurgy, 61(2), 267-279. Retrieved from https://aseestant.ceon.rs/index.php/jmm/article/view/59512
Issue
Vol. 61 No. 2 (2025)
Section
Original Scientific Paper

Authors retain copyright of the published papers and grant to the publisher the non-exclusive right to publish the article, to be cited as its original publisher in case of reuse, and to distribute it in all forms and media.

The Author(s) warrant that their manuscript is their original work that has not been published before; that it is not under consideration for publication elsewhere; and that its publication has been approved by all co-authors, if any, as well as tacitly or explicitly by the responsible authorities at the institution where the work was carried out. The Author(s) affirm that the article contains no unfounded or unlawful statements and does not violate the rights of others. The author(s) also affirm that they hold no conflict of interest that may affect the integrity of the Manuscript and the validity of the findings presented in it. The Corresponding author, as the signing author, warrants that he/she has full power to make this grant on behalf of the Author(s). Any software contained in the Supplemental Materials is free from viruses, contaminants or worms.

The published articles will be distributed under the Creative Commons Attribution ShareAlike 4.0 International license (CC BY-SA).

Authors are permitted to deposit publisher's version (PDF) of their work in an institutional repository, subject-based repository, author's personal website (including social networking sites, such as ResearchGate, Academia.edu, etc.), and/or departmental website at any time after publication.

Upon receiving the proofs, the Author(s) agree to promptly check the proofs carefully, correct any typographical errors, and authorize the publication of the corrected proofs.

The Corresponding author agrees to inform his/her co-authors, of any of the above terms.